FUN FACTS
How many years are we in business?
What is 115?
Where will our new Tsune cold saw be located?
Where is Cinnci?
What alloy is AMS5659?
What is 15-5?
What does VAR stand for?
What is Vacuum Arc Remelt?
What is the most popular alloy for gear manufacturing?
What is 9310?
What are the 5 Alloys in the AERO bar initiative?
What is 13-8, 15-5, 300M, 4340 & 9310?
Why is material heat treated?
What is improved material properties, refined grain structure & stress relieved?
What is 300 Modified also known as?
What is 4340 Modified?
Why would you want a VAR product?
What is cleaner & removes of gasses?
What Alloy is used in both landing gear & motorsports driveshafts?
What is 300M
How many pounds has TW purchased for this initative?
What is 8 million?
What are 3 value added processes TW can offer?
What is saw cutting, heat treating, trepanning, gun drilling?
Why would you need DFAR spec material?
What does the GOVT & their subs mandated to spec their alloys to?
What AERO alloy bar we stock has the highest NI content?
What is 13-8?
What PH alloy is a step up from
17-4?
What is 15-5?
What is the main Aerospace application for 13-8PH?
What is landing gear?
What is the difference between trepanning & gundrilling?
What process leaves the ID of the bar saved?
In what process is the starting electrode smaller than the ingot?
What is Vacuum Arc Remelting?
What does VIM stand for?
What is Vacuum Induction Melted?
What is the most expensive AERO alloy we will be stocking? And why is it so expensive?
What is 13-8?
Name 2 sections of an Aircraft where you would find an Actuator?
What is landing gear, cargo door......?
Name 3 of the 4 stages of heat treating?
What are charging matl, heat matl, hold matl at temp(soaking), cooling (quenching)?
Which 3 alloys in our program have predominantly iron in their chemistries?
What are 300M, 9310 & 4340?
Why would you spec a PH Alloy?
What gives material strength without quenching & tempering to avoid scaling, distortion?
What AERO bar alloy has approx. 0.40% carbon?
What is 4340?